MOMENT REDUCTION ANALYSIS OF BUILT-UP I-SECTION EXPOSED TO UNIFORM CORROSION
Author Info
Hotz, Carl
Permalink:
http://rave.ohiolink.edu/etdc/view?acc_num=akron1525293365942438
Abstract Details
Year and Degree
2018, Master of Science in Engineering, University of Akron, Engineering.
Abstract
With an aging infrastructure in the United States it is becoming more pressing to understand corrosion and the effects it has on structures. This knowledge will allow structural inspectors to determine the best course of action to take when dealing with a corroded member and insight so as to not take a member out of service prematurely. There are many types of corrosion that effects steel structures the form that is being studied in this report is uniform corrosion. Uniform corrosion occurs when the corrosion process attacks the surface of the steel uniformly thinning the material. This report looks at the effect uniform corrosion has on built up I sections subjected to a bending moment, and the reduction in moment strength associated with a percent loss in cross sectional area. To accomplish this lab tests were conducted on beams that were corroded in a controlled environment. With a known reduction in cross sectional area the beams were exposed to a bending test and the results were compared to moment values calculated using equations present in the American Institute of Steel Construction Steel Manual. In addition to bending tests tension tests were conducted on non-corroded tension specimens, corroded tension test specimens and corroded specimens that the corrosion byproduct was cleaned off by a chemical process. Finally finite element models were created to as another check and to see if the corrosion process could be modeled by assuming idealized uniform loss in area from corrosion
Committee
Anil Patnail, Dr. (Advisor)
Craig Menzemer, Dr. (Committee Member)
David Roke, Dr (Committee Member)
Pages
185 p.
Subject Headings
Civil Engineering
Keywords
Uniform Corrosion, I-Section, Structural Engineer, Moment Reduction, Finite Element Modeling, Tension Test, ASTM B117, Corrosion Tests, Environmental Chamber
Recommended Citations
Refworks
EndNote
RIS
Mendeley
Citations
Hotz, C. (2018).
MOMENT REDUCTION ANALYSIS OF BUILT-UP I-SECTION EXPOSED TO UNIFORM CORROSION
[Master's thesis, University of Akron]. OhioLINK Electronic Theses and Dissertations Center. http://rave.ohiolink.edu/etdc/view?acc_num=akron1525293365942438
APA Style (7th edition)
Hotz, Carl.
MOMENT REDUCTION ANALYSIS OF BUILT-UP I-SECTION EXPOSED TO UNIFORM CORROSION.
2018. University of Akron, Master's thesis.
OhioLINK Electronic Theses and Dissertations Center
, http://rave.ohiolink.edu/etdc/view?acc_num=akron1525293365942438.
MLA Style (8th edition)
Hotz, Carl. "MOMENT REDUCTION ANALYSIS OF BUILT-UP I-SECTION EXPOSED TO UNIFORM CORROSION." Master's thesis, University of Akron, 2018. http://rave.ohiolink.edu/etdc/view?acc_num=akron1525293365942438
Chicago Manual of Style (17th edition)
Abstract Footer
Document number:
akron1525293365942438
Download Count:
340
Copyright Info
© 2018, all rights reserved.
This open access ETD is published by University of Akron and OhioLINK.