STABILIZATION/SOLIDIFICATION TREATMENT OF MERCURY CONTAINING WASTES USING REACTIVATED CARBON AND CEMENT

ZHANG, JIAN
http://rave.ohiolink.edu/etdc/view?acc_num=ucin1035207019

Abstract Details

2002, PhD, University of Cincinnati, Engineering : Environmental Engineering.
This paper presents the study results for a novel stabilization/solidification (S/S) process for high mercury wastes (Hg > 260 ppm). A relatively low-cost powder reactivated carbon (PAC) was used to stabilize mercury in solid wastes. Then the stabilized wastes were subjected to cement solidification. To improve the mercury adsorption capacity, PAC was impregnated with sulfides to obtain sulfurized PAC (SPAC). It was found that sulfurization of PAC by both CS 2 and Na 2 S significantly improved the mercury stabilization efficiency. For a Hg(NO 3 ) 2 solution with 40 mg/L initial Hg 2+ , the equilibrium concentration of Hg 2+ was lowered to 110 μg/L by SPAC, compared with an equilibrium concentration of 4310 μg/L by PAC. The adsorption efficiency was increased by more than one order of magnitude. The mechanism of sulfurization on mercury adsorption was investigated. It is believed that formation of low solubility mercury-sulfide species was the major cause of this phenomenon. The cement-solidified wastes were subjected to TCLP leach testing and constant pH leach testing. For the constant pH leach testing, the wastes were leached at constant pH values of 2, 4, 6, 8, 10, and 12 for 14 days. From the experimental results, it was found that, once in the solidified waste form, SPAC particles retained most of the adsorbed mercury, even in the presence of high chloride concentration, possibly due to the build-up of a gel-membrane outside the carbon pores as the hydration of cement proceeded. Experimental results from constant pH leaching tests indicated that the stabilized and solidified wastes were quite stable over a wide pH range after 14 days. A model was developed to simulate mercury sorption by reactivated carbon in stirred batch reactors. The model involved the coupling of a pseudo-second order kinetic model, surface equilibrium models, including the Langmuir isotherm and the Freundlich isotherm, and a material balance equation based on batch reactors. The predicted and real carbon dosages match each other very well. It can be concluded that the S/S process by reactivated carbon and cement is a robust and effective technology for immobilization treatment of high mercury wastes.
Dr. Paul L. Bishop (Advisor)
160 p.
Engineering, Environmental
mercury; activated carbon; stabilization/solidification; sulfurization; cement

Recommended Citations

Citations

  • ZHANG, J. (2002). STABILIZATION/SOLIDIFICATION TREATMENT OF MERCURY CONTAINING WASTES USING REACTIVATED CARBON AND CEMENT [Doctoral dissertation, University of Cincinnati]. OhioLINK Electronic Theses and Dissertations Center. http://rave.ohiolink.edu/etdc/view?acc_num=ucin1035207019

    APA Style (7th edition)

  • ZHANG, JIAN. STABILIZATION/SOLIDIFICATION TREATMENT OF MERCURY CONTAINING WASTES USING REACTIVATED CARBON AND CEMENT. 2002. University of Cincinnati, Doctoral dissertation. OhioLINK Electronic Theses and Dissertations Center, http://rave.ohiolink.edu/etdc/view?acc_num=ucin1035207019.

    MLA Style (8th edition)

  • ZHANG, JIAN. "STABILIZATION/SOLIDIFICATION TREATMENT OF MERCURY CONTAINING WASTES USING REACTIVATED CARBON AND CEMENT." Doctoral dissertation, University of Cincinnati, 2002. http://rave.ohiolink.edu/etdc/view?acc_num=ucin1035207019

    Chicago Manual of Style (17th edition)

ucin1035207019
1,296
© 2002, all rights reserved.
This open access ETD is published by University of Cincinnati and OhioLINK.